HV220 7.10g/Cm3 Ceramic Kilns FeCrAl Heating Wire

Shanghai Tankii Alloy Material Co.,Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment

HV220 7.10g/Cm3 Ceramic Kilns FeCrAl Heating Wire

Brand Name : TANKII

Model Number : TK-APM 216YZ

Certification : ISO SGS

Place of Origin : Shanghai, China,

MOQ : 10KG

Price : negotiable

Payment Terms : L/C, T/T, Western Union

Supply Ability : 100 Tons per Month

Delivery Time : 7-15 work days

Packaging Details : wooden case

Material : Iron-Chromium-Aluminum Alloy

Max. Use temper. : 1420℃ / 2588°F

Diameter : 0.10-8.50mm

Sample order : Accepted

Surface : Bright / Oxidation / Golden

Density : 7.10g/cm3

Resistivity : 1.45µΩ.m

Similar grades : Kan-thal APM, APM, TK-APM, TK-APM216YZ,

Contact Now

High-temperature Heating FeCrAl APM / TK-APM 216YZ Iron Chromium Aluminum Alloy Wire for ceramic kilns

TK-APM 216YZ Iron Chromium Aluminum Alloy takes refined master alloy as raw material, uses powder metallurgy technology to manufacture alloy ingots, and is manufactured by special cold and hot processing and heat treatment process. The product has the advantages of strong oxidation resistance, good corrosion resistance at high temperature, small creep of electrothermal components, long servicelife at high temperature and small change of resistance. It is suitable for high temperature 1420,high power density, corrosive atmosphere, carbon atmosphere and other working environments. It can be used in ceramic kilns, high temperature heat treatment furnaces, laboratory furnaces,electronic industrial furnaces and diffusion furnaces.

Main mechanical properties

Tensile Strength at Room Temperature: 650-750MPa

Elongation rate: 15-25%

hardness: HV220-260

Tensile Strength at 1000℃ Temperature 22-27MPa

High Temperature Durability at 1000 Temperature and 6MPa ≥100h

Mainly composition(Wt%)

C Si Mn Cr Al Fe
Min - - - 20 5.5 Bal.
Max 0.04 0.5 0.4 22 6.0 Bal.

Mainly physical properties

density 7.10g/cm3

resistivity 1.45µΩ.m

Resistance Temperature Coefficient(Ct)

800℃ 1000℃ 1400℃
1.03 1.04 1.05

Average linear expansion coefficient()

20-800℃ 20-1000℃ 20-1400℃
14 15 16

Maximum Continuous Working Temperature 1400℃

Fast life

1300℃ 1350℃

Average Fast Life (Hours)

110 90

Sagging rate after rupture

8 11

Noted:Testing according to GB/T13300-91 standard method

HV220 7.10g/Cm3 Ceramic Kilns FeCrAl Heating Wire

  • Rated Voltage: 220V/380V

  • The installation process to avoid knocking, to avoid the damp, hand-held stove wire, they should wear gloves. Wire should be installed after the furnace has remained flat, and prevent surface scratches, dirt, corrosion, or improper installation, by affecting the life of

  • In the rated voltage to use. In strong reducing atmosphere, acid atmosphere, an atmosphere of high humidity will affect the use of life;

  • Temperature before use should be in dry non-corrosive atmosphere, about 1000 ℃ spend a few hours, so that furnace wire protective film formed on the surface after normal use, so that can guarantee the normal life of furnace wire;

  • Furnace installation should ensure that the insulated wire good power to avoid touching furnace after the wire, guard against electric shock or burns.

Specifications

Wire diameter range: φ0.1-8.5mm


Product Tags:

FeCrAl Heating Wire

      

Ceramic Kilns Heating Wire

      

HV220 Heating Wire

      
Quality HV220 7.10g/Cm3 Ceramic Kilns FeCrAl Heating Wire for sale

HV220 7.10g/Cm3 Ceramic Kilns FeCrAl Heating Wire Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Shanghai Tankii Alloy Material Co.,Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)